    Applicability of Paper and Pulp Industry Waste for Manufacturing Mycelium-Based Materials for Thermoacoustic Insulation
    (2024) Munoz, Hugo; Molina, Paulo; Urzua-Parra, Ignacio A.; Vasco, Diego A.; Walczak, Magdalena; Rodriguez-Grau, Gonzalo; Chateau, Francisco; Sancy, Mamie
    Cellulose and paper produce significant waste such as ash, activated sludge, and sludge from the pulp and paper industry. Depending on the raw material, legislation, and subprocesses, these sludges contain around 30-50% organic matter, mainly composed of less than 0.02 mm cellulose fibers and hemicellulose and lignin. This work used sludge from the pulp and paper industry as a substrate for manufacturing mycelium-based biomaterials using the white rot fungus Trametes versicolor. Chemical and surface analyses revealed the formation of new materials. Acoustic impedance analyses revealed that these materials have a noise reduction coefficient and sound absorption average comparable to extruded polystyrene and polyurethane. In addition, the material's thermal conductivity was near that of sheep wool. Therefore, the biomaterials fabricated using sludge and Trametes versicolor have the potential to be a game-changer in the industry as promising thermoacoustic insulators.
  • No Thumbnail Available
    Item
    The Effect of the Addition of Copper Particles in High-Density Recycled Polyethylene Matrices by Extrusion
    (2022) Arcos, Camila; Munoz, Lisa; Cordova, Deborah; Munoz, Hugo; Walter, Mariana; Azocar, Manuel I.; Leiva, Angel; Sancy, Mamie; Rodriguez-Grau, Gonzalo
    In this study, the effect of the recycling process and copper particle incorporation on virgin and recycled pellet HDPE were investigated by thermo-chemical analysis, mechanical characterization, and antibacterial analysis. Copper particles were added to pellet HDPE, virgin and recycled, using a tabletop single screw extruder. Some copper particles, called copper nano-particles (Cu-NPs), had a spherical morphology and an average particle size near 20 nm. The others had a cubic morphology and an average particle size close to 300 nm, labeled copper nano-cubes (Cu-NCs). The thermo-chemical analysis revealed that the degree of crystallization was not influenced by the recycling process: 55.38 % for virgin HDPE and 56.01% for recycled HDPE. The degree of crystallization decreased with the addition of the copper particles. Possibly due to a modification in the structure, packaging organization, and crystalline ordering, the recycled HDPE reached a degree of crystallization close to 44.78% with 0.5 wt.% copper nano-particles and close to 36.57% for the recycled HDPE modified with 0.7 wt.% Cu-NCs. Tensile tests revealed a slight reduction in the tensile strength related to the recycling process, being close to 26 MPa for the virgin HDPE and 15.99 MPa for the recycled HDPE, which was improved by adding copper particles, which were near 25.39 MPa for 0.7 wt.% copper nano-cubes. Antibacterial analysis showed a reduction in the viability of E. coli in virgin HDPE samples, which was close to 8% for HDPE containing copper nano-particles and lower than 2% for HDPE having copper nano-cubes. In contrast, the recycled HDPE revealed viability close to 95% for HDPE with copper nano-particles and nearly 50% for HDPE with copper nano-cubes. The viability of S. aureus for HDPE was lower than containing copper nano-particles and copper nano-cubes, which increased dramatically close to 80% for recycled HDPE with copper nano-particles 80% and 75% with copper nano-cubes.